Series alumina sphaerica HRK producitur ab caliditate liquamenti methodi in Al2O3 irregulari in modum enucleandi, et deinde protegendo, purificatione et aliis processibus ad ultimum productum obtinendum subit.Alumina consecuta habet rate altam sphaeroidizationem, moderatricem particulam magnitudine distributionis et puritatem altam.Propter singulares proprietates suas sicut princeps scelerisque conductivity et mobilitatis bonae, Productum late usus est ut filler materiarum instrumentorum scelestarum, machinarum materiarum thermarum et aluminium substructio aeris-clad Laminates et cetera.
Technical item | Unitas | HRK Series product Code | ||||||||||
Magnitudo particula | HRK-1 | HRK-2 | HRK-5 | HRK-10 | HRK-20 | HRK-30 | HRK-40 | HRK-70 | HRK-90 | HRK-120 | ||
(D10) | µm | 0.71 | 0.69 | 2.54 | 4.55 | 10.5 | 16.88 | 23.77 | 44.32 | 55.23 | 92.39 | |
(D50) | µm | 1.08 | 2.18 | 5.52 | 10.43 | 20.8 | 30.52 | 41.54 | 71.54 | 87.96 | 122.98 | |
(D90) | µm | 3.21 | 5.24 | 9.09 | 20.8 | 37.24 | 48.87 | 66.44 | 106.5 | 134.92 | 172.07 | |
Imprimis Superficies | m2/g* | 1.69 | 1.27 | 0.36 | 0.17 | 0.14 | 0.13 | 0.12 | 0.12 | 0.1 | 0.06 | |
Electrical Conductivity | u S/cm* | 6.07 | 5.4 | 5.65 | 4.05 | 6.87 | 7.95 | 4.65 | 6.18 | 8.15 | 6.45 | |
PH Precium | - | 7.53 | 7.79 | 7.7 | 7.9 | 7.62 | 7.7 | 7.8 | 7.7 | 7.9 | 7.54 | |
umor | % | 0.05 | 0.03 | 0.03 | 0.03 | 0.03 | 0.03 | 0.03 | 0.03 | 0.03 | 0.04 | |
Verum densitas | g/cm3 | 3.71 | 3.7 | 3.74 | 3.76 | 3.79 | 3.79 | 3.81 | 3.87 | 3.88 | 3.89 | |
Spheroidization Rate | % | 96 | 98 | 98 | 98 | 96 | 98 | 96 | 96 | 95 | 95 | |
Compositio chemica | Al2O3 | % | 99.87 | 99.94 | 99.89 | 99.94 | 99.92 | 99.93 | 99.94 | 99.92 | 99.94 | 99.92 |
SiO2 | ppm | 430 | 30 | 430 | 20 | 150 | 20 | 20 | 30 | 20 | 170 | |
Fe2O3 | ppm | 140 | 70 | 140 | 40 | 60 | 60 | 50 | 60 | 60 | 140 | |
Na2O | ppm | 90 | 100 | 10 | 60 | 140 | 90 | 110 | 90 | 70 | 90 |
● Scelerisque instrumenti materias: scelerisque silica codex, scelerisque uncto, scelerisque potting gluten PROLIXUS, Phase mutatio materias;
● Thermally Conductive Engineering Plastics: DUCTUS lucerna operculum, transitum testam, testam electronic productam, electrica productorum calores dissipationis partes;
● Al-fundatur Copper Laminate Clad: summus potestas DUXERIT circuii substratum, potentia tabularum ambitum, etc;
● Alumina Filtra Ceramic;
Scelerisque Spray Coating.